Academic Journal of Engineering and Technology Science, 2019, 2(1); doi: 10.25236/AJETS.020013.
Haifei Lu1, 2, 3, Weiguang Tian1, 2, 3 and Jialin Xu1, 2, 3
1. Guangdong Guangqing Metal Technology Co., Ltd., Yangjiang, 529533, Guangdong, China
2. Guangdong Guangqing New Materials Research Co., Ltd., Yangjiang, 529533, Guangdong, China
3. Guangdong Provincial Key Laboratory of High Quality Stainless Steel Technology Research and Development, Yangjiang, 529533, Guangdong, China
Aiming at the transverse cracking defect of 304 stainless steel deep drawing product (rice cooker inner liner) in the process of deep drawing, the martensite content, metallographic structure and mechanical properties were tested. The morphology of 304 stainless steel deep drawing product was observed by scanning electron microscopy, and the components of the defect were analyzed by energy dispersive spectrometer. Based on the experimental results and related research and analysis, it is inferred that the cracking defect of stainless steel inner tank is mainly caused by work hardening in deep drawing process, and small crack is formed due to inclusion shedding in steel, and crack extends further in plastic deformation.
304 stainless steel, deep drawing, inner tank, crack
Haifei Lu, Weiguang Tian and Jialin Xu. Analysis of Surface Cracking Defect of 304 Stainless Steel Deep Drawing Products. Academic Journal of Engineering and Technology Science (2019) Vol.2, Num.1: 41-47.
[1] Li Shuhui. Current development and trends of the tailored blank application in auto-body stamping [J]. Journal of Mechanical Engineering, 2002, 38 (2): 1-7.
[2] Hu Limu, Hu Bo, Zhang Yonghong, et al. Analysis of corrosion resistance of A -TIG welded joint for austenitic stain less steel [J]. Transactions of the china welding institution, 2006, 27 (7): 34-36. (In Chinese)
[3] Yang Jianguo, Chen Shuangjian, Huangnan, et al. Factors affecting deformation induced martensitic transformation of SUS304 stainless steel [J]. Transactions of the china welding institution, 2012, 33 (12): 89-92. (In Chinese)
[4] Shi Kai, Jiang Haiyi. Effect of Deformed Martensite on Properties of Austenitic Stainless Steel Head [J]. China special equipment safety, 2014, 30 (2): 21-24. (In Chinese)
[5] Wu Zhuxian. Application Analysis of Baoxin’s Deep Drawing Products [J]. Baosteel Technology, 2009 (5): 8-11. (In Chinese)
[6] Wu Zhuxian, Wu Difeng, Liu Ming, et al. Analysis of causes of transverse cracking on side walls of 304 stainless steel products [J]. Baosteel Technology, 2014 (4): 33-37. (In Chinese)